CorrosionX HD Corrosion Inhibitor, Moisture Displacer & Lubricant

CorrosionX Heavy Duty Corrosion Inhibitor, Moisture Displacer & Lubricant

• CorrosionX® Heavy Duty (also widely known as CorrosionX HD) is a high performance thickened-film version of CorrosionX®. It was developed specifically to provide maximum protection against moisture intrusion and the resulting rust and corrosion.
• CorrosionX Heavy Duty is dripless and resists displacement or removal by splash, rain, seawater or even pressure washing. It is ideal for long-term protection against serious rust and corrosion assault and in situations where the surface being protected is exposed directly to the elements. Unlike wax-based corrosion inhibitor barrier coatings, CorrosionX HD will not dry, harden or crack. The coating is self-healing and will slowly penetrate existing rust and corrosion, displacing moisture and corrosion-causing electrolytes.

Physical Characteristics

Color
Light Brown
Volume Solids
97%
Appearance
Thin grease
VOC Content g/L(%)
30 (3)
Odor
Petroleum
Vapor Pressure, mm Hg @ 23°C
>1
Specific Gravity @ 15.6ËšC
0.911
Pour Point
-30°C / -22°F
Viscosity, cPs (#6 spindle at 6 rpm)
10,000 - 12,000
Solubility in Water
Negligible
Flash Point (COC)
132ËšC / 270ËšF
Boiling Point / Range
>218°C / 425°F
Coverage per gallon
up to 320 sq ft
Evaporation Rate (BuAc=1)
<0.01
Weight per gallon
7.3 lbs
Film Thickness
0.005"

Performance Properties

Corrosion Protection:

Salt Spry, hrs.
>2,000
ASTM B117
(Film Thickness)
5.5 mils
Humidity Cabinet, hrs.
>2,000
ASTM D1748

Panels were pulled from both the salt spray and humidity cabinets at 2,000 hrs. with no sign of rust.

Advantages

• Unlike wax-based corrosion inhibitor barrier coatings, the coating will not dry, harden or crack
• Self-healing and will slowly penetrate existing rust and corrosion, displacing moisture and corrosion-causing electrolytes.
• Dripless and resists displacement or removal by splash, rain, seawater or even pressure washing
• Ideal for long-term protection against serious rust and corrosion assault and in situations where the surface being protected is exposed directly to the elements.